Solid ammonia storage and delivery material

ABSTRACT

A solid ammonia storage and delivery material A solid ammonia storage material comprising: an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula: M a (NH 3 ) n X z , wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and ri is the coordination number of 2 to 12, wherein M is Mg provides a safe, light-weight and cheap compact storage for ammonia to be used in the automotive industry.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to the storage of ammonia in a solid form using metal ammine complexes and delivery there from. The invention also relates to the use of ammonia stored in a solid form as the reducing agent in selective catalytic reduction (SCR) of NO_(x) in exhaust gases from combustion processes, to methods for producing such complexes and to an ammonia delivery device comprising such complexes.

2. Description of the Related Art

Current environmental regulations necessitate the use of catalysts in the exhaust gas from automotive vehicles, boilers and furnaces for control of NO_(x) emission leaving the system. Particularly, vehicles equipped with diesel engines or other lean burn engines offer the benefit of improved fuel economy, but suffer from the drawback of increased formation of NO_(x) being noxious and which must be eliminated from the exhaust gas. However, catalytic reduction of NO_(x) using conventional so-called three-way exhaust catalysts for automobiles is impossible because of the high content of oxygen in the exhaust gas. Instead, selective catalytic reduction (SCR) has proven useful for achieving the required low levels of NO_(x) in the exhaust gas both in stationary and mobile units. In such systems NO_(x) is continuously removed from the exhaust gas by injection of a reducing agent into the exhaust gas prior to entering an SCR catalyst capable of achieving a high conversion of NO_(x). So far, ammonia has proven to be the most efficient reducing agent, which is usually introduced into the exhaust gas by controlled injection of gaseous ammonia, aqueous ammonia or aqueous urea. In all cases, the amount of reducing agent being dosed has to be very precisely controlled. Injection of a too large amount of reducing agent will cause emission of ammonia with the exhaust gas whereas injection of a too small amount of reducing agent causes a less than optimum conversion of NO_(x).

In many mobile units powered by combustion engines, the preferred technical solution is to use an aqueous solution of urea as the reducing agent since in this way potential hazards or safety issues relating to the transport and handling of liquid ammonia in high pressure containers are eliminated. However, there are several disadvantages related to the use of aqueous urea as the reducing agent. First of all, the use of urea solutions requires the carrying of a relatively large volume in order to provide sufficient amounts of ammonia to allow a vehicle to drive e.g. about 20,000 kilometres without having to substitute or refill the source of ammonia. In typical systems, an aqueous solution comprising about 30 wt % of urea is preferred meaning that about 70 wt % of the content of a container holding the urea solution is used only to transport water. During the decomposition, one molecule of urea forms two molecules of NH₃ and one molecule of CO₂ and thus, ammonia only constitutes roughly 50 wt % of the weight of the urea molecule and hence, the concentration of ammonia of the reducing agent is very low. Similar concentrations of ammonia can be achieved using aqueous solutions of ammonia as reducing agents. Furthermore, when using solutions, specially designed spray nozzles combined with a precision liquid pump are required to ensure that a) the aqueous urea is delivered to the exhaust system at a desired (and dynamically changing) flow rate and b) the aqueous urea is efficiently dispersed in the gas phase before entering the catalyst. Finally, the aqueous solutions might freeze in cold weather conditions (below minus 11° C.), or the urea solution may simply form precipitates, which will block the dosing system, e.g. the nozzle. Altogether, these difficulties may limit the possibilities of using SCR technology in abatement of pollution from NO_(x), particularly in connection with mobile units.

Transporting ammonia as a pressurized liquid is hazardous as the container may burst or a valve or tube might break in an accident giving a discharge of poisonous/lethal gaseous ammonia. In the case of the use of a solid storage medium containing absorbed/adsorbed ammonia, the safety issues are much less critical since a small amount of heat is required to release the ammonia from the storage medium.

International Patent Publication No. WO 99/01205 discloses a method and a device for selective catalytic NOx reduction in waste gases containing oxygen, using ammonia and a reduction catalyst. According to the method, gaseous ammonia is provided by heating a solid storage medium comprising one or more salts, especially a chloride and/or sulphate of one or more cations selected from alkaline earth metals, and/or one or more transition metals, preferably Mn, Fe, Co, Ni, Cu, and/or Zn, said storage medium being introduced into a container. In the preferred embodiments of WO 99/01205 the cation is Ca²⁺ or Sr²⁺. The inventive method and device are stated to be particularly suitable for use in automobiles.

However, the use of the ammonia storage media known from WO 99/01205 suffers from various draw-backs hampering a wide-spread use in the automotive industry. The vapour pressure of ammonia above a solid salt phase is e.g. about 1 bar at room temperature and atmospheric pressure for calcium octa ammine chloride and strontium octa ammine chloride complexes rendering the use somewhat complicated due to the high pressures that must be taken into account in view of the toxicity of ammonia. Having such a high partial pressure of ammonia, the handling and transportation of the saturated storage material is still difficult and also dangerous. Still further, the use of granulated storage materials—stated as preferred embodiments in WO 99/01205—requires measures for preventing the storage material from leaving the container during use in moving vehicles. Furthermore, a granulated material will have a considerable void between the granules which will drastically reduce the bulk density of the storage material by a factor 1.5-2.

It has now been found that these drawbacks may be overcome using a magnesium salt complex according to the present invention providing a compact, light-weight, cheap and more safe storage for ammonia having a very low vapour pressure of ammonia below 0.1 bar at room temperature to be used in the automotive industry.

SUMMARY OF THE INVENTION

The present invention relates to a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg.

In a second aspect the invention relates to a method of producing a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said method comprising the steps of 1) providing the solid salt, 2) saturating the salt with ammonia, and 3) compressing the ammonia salt complex.

In a third aspect the invention relates to a method for selective catalytic NO_(x) reduction in waste gases containing oxygen, using ammonia and a reduction catalyst wherein gaseous ammonia is provided by heating a solid storage medium comprising one or more ionic ammonia absorbing salts of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and transition metals such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions such as chloride or sulphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg and wherein the release rate of ammonia is controlled in consideration of the content of NO_(x) in the waste gases.

In a fourth aspect the invention relates to the use of a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and transition metals such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions such as chloride or sulphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg as a source of ammonia as the reducing agent in selective catalytic reduction (SCR) of NO_(x) in exhaust gases from combustion processes.

In a fifth aspect the invention relates to an ammonia delivery device comprising a container comprising

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg, said container being provided with one or more closable outlet opening(s) connected to a pipe and further being provided with means for heating the container and the ammonia absorbing salt for release of gaseous ammonia.

In a sixth aspect the invention relates to the use of an ammonia delivery device comprising a container comprising

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg, said container being provided with one or one or more closable outlet opening(s) connected to a pipe and further being provided with means for heating the container and the ammonia absorbing salt for release of gaseous ammonia as a source for ammonia in selective catalytic reduction of NO_(x) in exhaust gases from combustion processes.

In a seventh aspect the invention relates to a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkali metals, alkaline earth metals, and transition metals such as Li, Na, K, Cs, Mg, Ca, V, Cr, Mn, Fe, Co, Ni, Cu, or Zn or combinations thereof such as NaAl, KAI, K₂Zn, CsCu, or K₂Fe, X is one or more anions selected from fluoride, chloride, bromide, iodide, nitrate, thiocyanate, sulphate, molybdate, and phosphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said storage and delivery material having a density of 0.9 to 1.3 g/cm³.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention is disclosed more in detail with reference to the drawings in which

FIG. 1 shows a photograph of an ammonia delivery device of the invention,

FIG. 2 shows schematically a top view of the location of thermocouples in the device of FIG. 1,

FIG. 3 shows a diagram of the experimental setup,

FIG. 4 shows a graphical representation of the desorption of the ammonia,

FIG. 5 is a plot of the buffer pressure during desorption of the ammonia,

FIG. 6 shows the pressure and flow in a single pressure oscillation period during desorption,

FIG. 7 schematically shows a device for compression of an ammonia delivery material,

FIG. 8 schematically shows an embodiment of an ammonia delivery device of the invention,

FIG. 9 schematically shows another embodiment of an ammonia delivery device of the invention,

and FIG. 10 shows an equilibrium phase-diagram for the MgCl₂—NH₃ system.

DETAILED DESCRIPTION OF THE PRESENT INVENTION

The present invention is related to the use of metal-ammine salts as safe and efficient solid storage media for storage and controlled delivery of ammonia, which in turn is used as the reduction agent in selective catalytic. reduction to reduce NO_(x) emissions, especially from automotive vehicles, boilers and furnaces.

The present invention relates to a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg.

Suitable anions to be used according to the present invention may be selected from fluoride, chloride, bromide, iodide, nitrate, thiocyanate, sulphate, molybdate, and phosphate ions. The anion is preferably the chloride.

A preferred solid ammonia delivery material according to the invention is Mg(NH₃)₆Cl₂.

It has been found that although Mg(NH₃)₆Cl₂ has a very low partial pressure of ammonia above a salt phase, below 0.1 bar at room temperature, it is very suitable for use as a source of ammonia in SCR technology for abatement of pollution from NO_(x).

A solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions selected from chloride and sulphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, and the use thereof are also considered aspects of the present invention.

An ammonia saturated material of the invention may be prepared by exposing the dry salt to gaseous ammonia in a manner known per se. The ammonia saturated delivery material as prepared is powdery and rather “fluffy” and difficult to handle or transport and may be—during transport or use—transformed into small particle fragments thereby potentially blocking the dosing system of a device or give rise to hazardous dust into the environment. Furthermore, the powder has a low bulk density.

In a preferred embodiment of the invention the solid delivery material has a density of 0.9 to 1.3 g/cm³, more preferred a density of 1.1 to 1.3 g/cm³ giving a very high-density storage and delivery material.

The compacted material shows a very low release rate of ammonia at room temperature and atmospheric pressure and may be handled without special precautionary measures for protection against the action of ammonia. The compacted material can easily be handled during transport and during and after the final application.

It has surprisingly been found that a powdered ammonia delivery material of the present invention having a very low vapour pressure of ammonia at room temperature may be compacted to a very high density using several different methods for shaping of the material into a desired form and still be capable of delivery of ammonia at a sufficient rate to be suitable for use as a source of ammonia for a SCR reduction of NOx in e.g. automotive vehicles, boilers and furnaces. Such methods are e.g. pressing, extrusion, and injection moulding. In the case of pressing, a pressure might be applied in several different ways in a manner known per se. In one embodiment, the material is compressed to shapes like dense blocks or tablets by placing the saturated salt in a groove/dent/hole/pit in a metal block (e.g. in a cylindrical hole) and applying pressure to compress the material using a corresponding piston.

The saturated material is preferably compressed to a bulk density above 70%, more preferred above 80% and even more preferred above 85%, of the skeleton density. In a preferred embodiment the present invention is related to the compaction and shaping of the saturated ammonia delivery material.

When an ammine complex of a salt is compressed to such a high extent, desorption from such a compacted material would be expected to be extremely slow, mostly due to diffusion hindrance. In most dense materials desorption of ammonia would involve solid state diffusion which is known to be a slow process for virtually all materials. This has surprisingly been found not to be the case for the dense materials according to the present invention. It has been found that when ammonia desorbs, a progressing nano-porous structure is formed as the “reaction front” proceeds, leaving open paths for additional ammonia to leave from the central parts of the body of storage material. This is in contrast to e.g. classical heterogeneous catalysis where conversion of reactants is only possible, if reactants are able to diffuse into the catalyst pore structure and the products are able to diffuse out of the catalyst pore structure.

The metal-ammine salts constitute a solid storage medium for ammonia, which represent a safe, practical and compact option for storage and transportation of ammonia (a single-crystalline compound of Mg(NH₃)₆Cl₂ has an ammonia density of 38 kmole NH₃/m³, whereas that of liquid ammonia is only slightly higher (40 kmole NH₃/m³)). Ammonia may be released from the metal ammine salt by heating the salt to temperatures in the range from 10° C., to the melting point of the metal salt ammine complex, preferably to a temperature from 100 to 700° C., more preferred to a temperature from 150 to 500° C.

During release of ammonia the metal-ammine salt of the formula M_(a)(NH₃)_(n)X_(z) wherein M, X, a, n, and z has the meaning stated above, is gradually transformed into a salt of the formula M_(a)(NH₃)_(m)X_(z) wherein 0≦m<n. When the desired amount of ammonia has been released, the resulting salt of formula M_(a)(NH₃)_(m)X_(z) can usually be converted back into the salt of the formula M_(a)(NH₃)_(n)X_(z) by treatment with a gas containing ammonia.

Anhydrous MgCl₂ absorbs up to six moles of NH₃ (Gmelins Handbuch, 1939; Liu, 2004) according to reactions 1 to 3:

MgCl₂(s)+NH₃(g)

Mg(NH₃)Cl₂(s)  (1)

Mg(NH₃)Cl₂(s)+NH₃(g)

Mg(NH₃)₂Cl₂(s)  (2)

Mg(NH₃)₂Cl₂(s)+4NH₃(g)

Mg(NH₃)₆Cl₂(s)  (3)

Typical ammonia contents of the metal ammine complexes are in the range of 20-60 wt %, and preferred complexes comprise above 30 wt % ammonia, more preferred above 40 wt % ammonia. The inexpensive compound Mg(NH₃)₆Cl₂ contains 51.7 wt % ammonia.

The present invention offers ammonia storage at significantly higher densities (both on a volume and a weight basis) than both aqueous ammonia and aqueous urea. For several metal ammine salts it is possible to release all ammonia and then transform the resulting material back into the original metal ammine salt in a large number of cycles. Additionally, the ammonia is directly delivered into the exhaust pipe as a gas, which is an advantage in itself—both for the simplicity of the flow control system and for an efficient mixing of reducing agent, ammonia, in the exhaust gas—but it also eliminates possible difficulties related to blocking of the dosing system because of precipitation in the liquid-based system.

Some metal ammine complexes offer a further advantage in that the vapour pressure of ammonia above a solid salt phase is relatively low. It is preferred that the vapour pressure is below 0.1 bar at room temperature, preferably below 0.01 bar. Specifically for Mg(NH₃)₆Cl₂ the vapour pressure is as low as 0.002 bar at room temperature and atmospheric pressure which in practice eliminates any noxious effect of the ammonia as the release of ammonia is as low or lower than the release from common cleaning materials containing ammonia.

For Mg(NH₃)₆Cl₂ the partial pressure of ammonia at room temperature is 0.002 bar. Even though a partial pressure of ammonia of 0.002 bar at ambient temperature in itself could cause health problems, the compacted material according to the invention saturated with ammonia releases ammonia at a very slow rate at ambient temperature and an equilibrium pressure of 0.002 bar will only be obtained after a considerable span of time, even if the material is placed in a very confined space. However, when raising the temperature e.g. in the delivery device, a quite quick desorption of ammonia is observed as discussed above.

For mobile units, it is particularly useful to use an ammonia delivery device comprising a container containing the metal ammine complex as such a container may easily be separated from mobile unit and replaced by a fresh at suitable intervals. In preferred embodiments, the metal ammine containers are recycled and recharged with ammonia in a separate recharging unit.

Due to the slow release of ammonia in open atmosphere at ambient temperatures for the compressed materials of the present invention, the handling of the materials does not require extensive safety precautions and substitution of exhausted storage and delivery material with fresh material does not require an encapsulation of the material facilitating the handling as compared to the handling of the materials used in the methods of the state of the art.

In another aspect the invention relates to a method of producing a solid ammonia storage and delivery material comprising an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said method comprising the steps of 1) providing the solid salt, 2) saturating the salt with ammonia, and 3) compressing the ammonia salt complex to a dense, shaped body.

In a preferred embodiment of the method of the invention, the ammonia salt complex is compressed to a density of 0.9 to 1.3 g/cm³, more preferred to a density of 1.1 to 1.3 g/cm³

In a further aspect the invention relates to a method of selective catalytic NO_(x) reduction in waste gases containing oxygen, using ammonia and a reduction catalyst wherein gaseous ammonia is provided by heating a solid storage and delivery medium comprising one or more ionic ammonia absorbing salts of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and transition metals such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg and wherein the release rate of ammonia is controlled in consideration of the content of NO_(x) in the waste gases.

In a yet further aspect the invention relates to the use of a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and transition metals such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg as a source of ammonia as the reducing agent in selective catalytic reduction (SCR) of NO_(x) in exhaust gases from combustion processes.

In yet another aspect the invention relates to an ammonia delivery device comprising a container comprising

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg, said container being provided with one or more closable outlet opening(s) connected to a pipe and further being ing provided with means for heating the container and the ammonia absorbing salt for release of gaseous ammonia.

In the ammonia delivery device according to the invention, the closure of the closable outlet opening(s) may be in the form of one or more valve(s) known per se for use in connection with ammonia.

Heating means may be in the form of an electrical resistive heating device known per se.

The heating means may alternatively be provided as heat produced by chemical reactions.

The salt is normally heated to temperatures in the range from 10° C. to the melting point of the metal salt ammine complex, preferably to a temperature from 100 to 700° C., more preferred to a temperature from 150 to 500° C.

In a preferred embodiment of the invention the release rate of ammonia is controlled by accurate control of the heating of the container and the ammonia absorbing salt for release of gaseous ammonia. The release of ammonia is preferably further controlled by reduction valves, flow controllers or similar equipment or units. The release of ammonia from a container is preferably controlled by interaction with an electronic engine control system for delivery of an optimum amount of ammonia in a specific ratio (e.g. NH₃:NOx=1:1) of the changing emission of NOx from the engine.

In still another aspect the invention relates to the use of an ammonia delivery device comprising a container comprising

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg, said container being provided with one or more closable outlet opening(s) connected to a pipe and further being provided with means for heating the container and the ammonia absorbing salt for release of gaseous ammonia as a source for ammonia in selective catalytic reduction of NO_(x) in exhaust gases from combustion processes.

In yet a further aspect, the invention relates to a solid ammonia storage and delivery material comprising:

an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkali metals, alkaline earth metals, and transition metals such as Li, Na, K, Cs, Mg, Ca, V, Cr, Mn, Fe, Co, Ni, Cu, or Zn or combinations thereof such as NaAl, KAl, K₂Zn, CsCu, or K₂Fe, X is one or more anions selected from fluoride, chloride, bromide, iodide, nitrate, thiocyanate, sulphate, molybdate, and phosphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said storage and delivery material having a density of 0.9 to 1.3 g/cm³.

Still further, the invention relates to a method of producing a solid ammonia storage and delivery material comprising an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula:

M_(a)(NH₃)_(n)X_(z),

wherein M is one or more cations selected from alkali metals, alkaline earth metals, and transition metals such as Li, Na, K, Cs, Mg, Ca, V, Cr, Mn, Fe, Co, Ni, Cu, or Zn or combinations thereof such as NaAl, KAl, K₂Zn, CsCu, or K₂Fe, X is one or more anions selected from fluoride, chloride, bromide, iodide, nitrate, thiocyanate, sulphate, molybdate, and phosphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said storage and delivery material having a density of 0.9 to 1.3 g/cm³, said method comprising the steps of 1) providing the solid salt, 2) saturating the salt with ammonia, and 3) compressing the ammonia salt complex to a density of 0.9 to 1.3 g/cm³.

The present invention is especially suitable for use in reduction of emission of NO_(x) in exhaust gases from stationary and mobile combustion engines or power plants fuelled by diesel oil, petrol, natural gas or any other fossil fuels.

Thus, the present invention is also especially suitable as a source for providing ammonia in selective catalytic reduction in exhaust gasses for reduction of emission from stationary and mobile combustion engines or power plants fuelled by methanol, ethanol, hydrogen, methane, ethane or any other synthetic fuels.

Mobile combustion engines for which the invention is suitable are may e.g. be automobiles, trucks, trains, ships or any other motorised vehicle.

The invention is particularly suitable for use in connection with reduction of NO_(x) in combustion gases from automobiles and trucks.

Stationary power plants for which the invention is suitable are preferably power plants generating electricity.

The present invention is also especially suitable for use in reduction of emission of NO_(x) in exhaust gases from solid oxide fuel cells (SOFC). SOFC's are operated at a high temperature, where there may be a small production of NO_(x), which can be removed by adding ammonia using the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The invention is now explained more in detail with reference to the drawings showing preferred embodiments of the invention.

Materials and Methods

MgCl₂ powder: anhydrous, >98% purity, Merck Schuchardt.

Glove-bag: Aldrich premium AtmosBag from Aldrich Chemical Company, Inc., 1001 West Saint Paul Ave., Milwaukee, Wis. 53233, USA.

Ammonia Gas: Ammonia Gas 99.9% from Hede Nielsen, Industriparken 27-31, 2750 Ballerup, Denmark.

Preparation of Ammonia Saturated MgCl₂ Powder.

The ammonia carrier, Mg(NH₃)₆Cl₂, was prepared by placing MgCl₂ powder for several days in a glove-bag containing ammonia gas at atmospheric pressure (1 bar) and at room temperature. The degree of saturation was checked by temperature programmed desorption (TPD) and verified to be near 100% of the theoretical amount. The absorption/desorption was found to be fully reversible.

The rate of absorption is dramatically increased at higher NH₃ pressures (minutes rather than days) (Touzain and Moundamga-lniamy, 1994).

An equilibrium phase-diagram of the MgCl₂—NH₃ system is shown in FIG. 10 also showing the process of saturation when carried out at 5 bars.

Starting from point B′ (pure MgCl₂) the pressure was increased to 5 bars at point A corresponding to an isothermal absorption at T=298.15K and resulting in the formation of fully saturated Mg(NH₃)₆Cl₂. The rate of formation depends on the equilibrium pressure drop; however absorption is generally quite fast at ammonia pressures of more than 4 bars (Touzain and Moundamga-Iniamy, 1994). As mentioned, the desorption reaction only proceeds at elevated temperatures, which is also indicated on the path from A to B (isobaric desorption at P=5 bar).

Example 1

An ammonia delivery device was made from stainless steel in the form of a cylindrical container, having the dimensions 2R0=H=10 cm, where R0 is the inner radius and H is the height of the reactor. A photograph of the device is shown in FIG. 1. The device was provided with five wells for insertion of thermocouples placed perpendicular to the tangent of the reactor circumference for determining the radial temperature distribution. Furthermore, a thermocouple was placed on the outer wall to measure the actual temperature of the heated steel wall. Ammonia-saturated MgCl₂ powder (258.8 grams) was then placed and compacted slightly by manual pressure to a bed density of approximately 331 kg/m³. A thin sheet of quartz cotton was placed on top of the salt to prevent any grains from being carried out of the reactor. As desorption of ammonia from the complex requires elevated temperature, a heating wire was wrapped around the reactor and thermal insulation (Rockwool) was placed on top of this. Using a PC with labview interface, the power to the heating tape surrounding the storage container was turned on/off when the pressure in the buffer was below/above the pressure set-point. The desorbed gaseous ammonia flowed into a small buffer container, that was placed after the desorption unit and having a volume of approximately 200 millilitres. The pressure inside the buffer was measured using a digital Kobold SEN-87 pressure meter. The position of the thermocouples (denoted T1 to T5) are shown in the below table 1 and illustrated in FIG. 2.

TABLE 1 Radial position of five thermocouples Thermocouple Radial distance from inner wall (mm) T1 0 (inner wall) T2 12 T3 26 T4 45 T5 50 (centre) The total test setup is shown in FIG. 3.

A mass-flow controller (Brooks Smart Mass Flow 5850S calibrated to NH₃) dosed the ammonia from the buffer container into a “tailpipe” conveying a stream of carrier gas of air (1000 litres/minute) corresponding roughly to the current of exhaust gas from a small car. In addition to dosing ammonia, the same device also measured the actual flow through the valve in millilitres/minute (at T=298.15 K and P=1 bar). According to the stoichiometry of the SCR reaction, the mixture ratio between NH₃ and NOx should be approximately 1:1 (e.g. (Koebel and Kleeman, 2000; Fang and DaCosta, 2003)). The transient NOx concentration (and by that the transient NH3 concentration) in the exhaust gas from a car is very complicated to describe a continuous mathematical function and as an approximation, a sinusoidal function was used. The amplitude was set to 210 millilitres/minute and the period was set to 120 seconds. Due to limitations in the dynamics of the mass-flow controller, however, the resulting outlet flow was not completely sinusoidal. Heating of the desorption unit was controlled using the ON-OFF controller programmed along with the datacollection in Labview. The control parameter was chosen as the buffer pressure and the set-point pressure was set to 5 bars. At such high pressures it is fairly safe to assume that there is no pressure gradient across the porous bed (Lu and Spinner, 1996), and therefore the reactor pressure should be equal to the buffer pressure. It is possible to reduce the set-point pressure, which will reduce the temperature required for desorption. However, the main reason for the choice of set-point pressure was to maintain a well-defined flow through the mass-flow controller. With proper flow-mapping the flow through the valve should in principle be independent of the back-pressure.

The result of the experiment appears from FIG. 4 which shows a graphical representation of recorded temperature at positions T1 and T5 (the melting point for MgCl₂ is 714° C.) during desorption of ammonia from the ammonia-saturated MgCl₂ powder, and FIG. 5 shows the recorded pressure in the buffer container during the experiment. Phases I-IV and an intermediate phase (phase (II-III)) have been indicated in FIGS. 4 and 5 and are explained more in detail below.

During the experiment, a controller increased the temperature of the unit slowly to sustain a desired pressure of ammonia in the buffer. In the case of the experiment in FIGS. 4 and 5, the buffer was kept at a pressure close to 5 bars. Other experiments were done at lower buffer pressures. This resulted in a lower operating temperature due to the thermodynamics of the storage material. A higher ammonia pressure gives a higher desorption temperature.

Phase (I)-Warm-up

During this phase the pressure was allowed to build up to the set-point, no ammonia was extracted during this initial warm-up phase.

Phase (II)—Desorption of First Four Moles of Ammonia

When reaching the set-point buffer pressure, heating was turned off and the mass-flow controller began to dose ammonia. This eventually caused the pressure to drop and heating was turned on again. Switching between on and off for dosing ammonia caused the pressure to oscillate around the set-point. The small oscillations in the measured out-flow (nearly sinusoidal flow) can also be seen in the large oscillations around the set-point, as it is shown in FIG. 6.

The large (and slow) oscillations are also seen in the temperature, and due to the low effective thermal conductivity of the porous solid matrix this is most pronounced in the vicinity of the source of heat (T1). During phase II, the oscillations of the pressure and temperature continued to increase in amplitude and decrease in frequency. Combined with the large temperature gradients observed from FIG. 4 this indicates, that the reaction proceeds along an inward moving reaction front. Such a moving front will increase the way of heat-transfer, which will result in increasing amplitude and decreasing frequency of the pressure/temperature oscillations.

Phase II-III—Transition Phase

As the front moves toward the centre of the reactor, less and less ammonia is available for desorption. Eventually, a new front builds up near the heat-source, in which the fifth mole of coordinated ammonia is desorbed. This again reduces the way needed for heat-transfer and thus reduces the amplitude and increases the frequency of the oscillations. The apparently lower amplitude of the oscillations in the transition phase as compared to phase III, indicates that there still is ammonia bound as Mg(NH₃)₆Cl₂ left for desorption near the centre.

Phase III—Desorption of Fifth Mole of Ammonia

The sudden increase of the amplitude marks the end of the transition phase and the beginning of the third phase, in which only the fifth mole of ammonia desorbed. The decrease of the pressure overshoot as compared to phase II is most obviously due to the fact that only one mole of ammonia was released as compared to the four moles released during phase II (cf. reactions 2 and 3), therefore reducing the overall desorption rate. However, the increased loss of heat to the surroundings due to the higher temperature level at T1 could also help moderating the temperature/pressure peaks. During this phase it is difficult to see any increase of amplitude and decrease of frequency of the pressure oscillation; however the peak temperature does increase throughout the phase.

Phase IV—Desorption of Sixth Mole of Ammonia

The amplitude of the pressure overshoot was even smaller during this phase than for phase II. One mole of ammonia was desorbed in both phase III and IV, but the increased loss of heat at T1 during phase IV helped moderating the temperature peaks and hence, also the overshoot of pressure. Since this experiment was run for several hours, including a night, a maximum allowable temperature of 500° C. was set as a safety parameter. From FIGS. 4 and 5 it can be seen, that this temperature was reached, which resulted in the loss of buffer pressure. As this occurred during the night, it was not corrected until the following morning by setting the maximum allowable temperature to 650° C. (64° C. less than the melting point temperature of MgCl₂). The temperature and pressure fluctuated a somewhat during this phase. This might indicate some sort of build-up of pressure and subsequent release due to mass-transfer hindrance. During phase IV, the temperature throughout the reactor became quite high. However, in an optimized system the set-point for pressure will certainly be lower than the chosen 5 bars, which will also reduce the required temperature for all three desorption reactions to occur.

Integration of the outlet flow curve in time yields the total accumulated volume of NH₃ released through the valve. This value can be converted to number of moles by means of the ideal gas law. In order for the process to be efficient, this value should be close to the theoretically predicted amount of NH₃ contained in the salt. This is easily calculated, since the ratio of MgCl₂ and NH₃ in a 100% saturated salt is 1:6. The stoichiometric calculations showed that, theoretically, 7.88 moles of ammonia should be stored within the given mass of Mg(NH₃)₆Cl₂ salt (258.8 grams), while the integration of the calibrated signal from the mass flow controller revealed that 7.86 moles of ammonia was released through controller giving a very high storage efficiency of approximately 99.8%.

Example 2 Compression of Solid Ammonia Storage Medium

FIG. 7 schematically shows a device compression of the solid ammonia delivery material for the preparation of cylindrical tablets (dimensions: 13 mm in diameter; 10 mm high). In this embodiment, the solid ammonia delivery material was compressed in a chamber by applying a pressure of 2-4 tons/cm² using a piston compressing the powdered saturated storage material. When the piston was removed, the delivery material was in the desired shape of e.g. a tablet, a cylinder or a rod, and had a density above 80% of the theoretical crystal density.

FIG. 8 schematically shows an embodiment of an ammonia delivery device of the invention for desorption of the compressed delivery material. In this embodiment, one or more tablets of solid ammonia delivery material 1 are placed in a container 2, which can be heated by a heating device 3. Desorbed ammonia leaves the container through a nozzle 4. Heat for the heating device 3 may be provided by e.g. resistive electric heating or chemical reactions. Such chemical reactions could be generated e.g. by combustion of a part of the released ammonia. If the delivery device is used in connection with SCR of NOx in exhaust gases, waste heat from the engine producing the gases can also be applied.

FIG. 9 schematically shows another preferred embodiment where only a part of the stored solid delivery material 1 is heated at a time. The solid delivery material is stored in compressed form, and introduced into a hot chamber 2 one at the time at intervals corresponding to the requirement for gaseous ammonia. The hot chamber is heated by a heating device 3 operated after the same principles as described above 2. Gaseous ammonia leaves the hot chamber through a nozzle 4, and when all ammonia is desorbed from a tablet 5 of solid ammonia delivery material, it is discarded into a separate container 6.

In a similar type of embodiment, the entire storage material is separated into a number of compartments each having their own heating source so that it is possible to have complete desorption of a given fraction of the material without using any moving parts to replace saturated/unsaturated salt e.g. on-board the vehicle during use.

The bed-density of the delivery material used in Example 1 was quite low (331 kg/m³ when compacted gently by hand) when compared to the density of MgCl₂ and Mg(NH₃)₆Cl₂ (1252 kg/m³, cf. the below table 2).

TABLE 2 Mass density Molar volume Salt kg/m³ cm³/mole Source MgCl₂ 2325 40.86 CRC Handbook 2004 Mg(NH₃)₆Cl₂ 1252 157.4 Gmelins Handbook 1939

A low density means that the entire storage system would require more space. This problem was solved by compressing Mg(NH₃)₆Cl₂ into solid rods having a density of 1219 kg/m³(97% of the solid density). TPD experiments confirmed that it was possible to desorp all ammonia from this tablet, thus increasing the potential storage capacity by a factor of 3.7 (on a molar basis) to approximately 93% of the volumetric ammonia storage capacity of liquid ammonia. A nearly quantitative desorption of ammonia from the dense material is possible because the front of desorption leaves behind a porous layer of anhydrous MgCl₂. This automatically generates the required pore system needed for mass-transfer through the structure. This is considered an ideal combination of a) an initially very compact structure having almost no void and being easy to handle, b) a high capacity for containing and delivering ammonia, c) a low external surface area, and d) a high degree of safety.

Example 3 Comparison of the Use of Ammonia Delivery Devices of the Invention and Urea-technology

By calculating the amount of NOx (assumed to be pure NO) generated per kilometre in a model fuel (taken as pure n-octane, ρ=696.8 kg/m3), the corresponding driving distance for a given amount of ammonia or urea can be found.

Based on the EURO 3 standards (The European Parliament, 1998) as well as by the values used by some researchers (Hyundai Motor Co.: Choi et al., 2001), the assumed NOx concentrations and the fuel economies are: 150 ppm and 10 km/litre for stoichiometric combustion (typically gasoline) and 300 ppm and 15 km/litre for lean burn combustion (λ=1.5, typically diesel).

Taking 1 litre (or 696.8 g) of fuel as a basis of calculations the generated NOx per. kilometre would be 5.87·10⁻² mole/km or 0.18 g/km for stoichiometric combustion, while for lean burn combustion (λ=1.5), the NOx emission is 1.15·10⁻² mole/km or 0.34 g/km.

In the below table 3 is shown the required mass/volume of the high-density Mg(NH₃)₆Cl₂ needed to drive 20,000 km (excluding the mass/volume of any equipment) compared to that of the 32.5% urea solution. The comparison is based on the combustion of pure n-octane and the above assumptions. The fuel is assumed to be pure n-octane and the exhaust is assumed to have an average molar fraction of 300 ppm NOx. The engine is assumed to run lean with a fuel economy of 15 km/litre fuel. The density of a 32.5% wt/wt urea solution is 1090 kg/m³ and the density of the Mg(NH₃)₆Cl₂ is assumed to be 1219 kg/m³.

TABLE 3 Mass/20,000 km Volume/20,000 km Material kg litre 1 Urea 21.2 19.4 2 Mg(NH3)₆Cl₂ 7.5 6.2 Ratio 1:2 2.8 3.1

The results clearly show the superior ammonia storage capacity of Mg(NH₃)₆Cl₂ over that of the urea solution. Combined with a high efficiency of approximately 99% this ammonia storage compound is very appropriate for the purpose. Due to the nature of the compaction of the materials, the present invention is also superior to the disclosures of WO 99/01205, where the preferred embodiment of granulated material of either Ca(NH₃)₈Cl₂ or Sr(NH₃)₈Cl₂ will results in a reduction in volumetric capacity of the theoretical salt densities by a factor of 1.5-2.

REFERENCES

-   Fang, H. L., DaCosta, H. F., 2003. Urea thermolysis and NOx     reduction with and without SCR catalysts. Applied Catalysis B:     Environmental 46, 17-34. -   Goetz, V., Marty, A., 1992. A model for reversible solid-gas     reactions submitted to temperature and pressure constraints:     Simulation of the rate of reaction in solid-gas reactor used as     chemical heat pump. Chem. Eng. Sci. 47 (17-18), 4445-4454. -   H. Van Vlack, L., 1989. Elements of Materials Science and     Engineering, sixth Edition. Addison-Wesley Publishing Company Inc. -   Hyundai Motor Co.: Choi, S.-m., Yoon, Y.-k., Kim, S.-j., Yeo, G.-k.,     Heesung Engelhard Corp.: Han, H.-s., 2001. Development of UREA-SCR     system for light-duty diesel passenger car. SAE Technical Paper     Series. -   Koebel, M.; Elsener, M., Kleeman, M., 2000. Urea-scr: A promising     technique to reduce NOx emissions from automotive diesel engines.     Catalysis Today 59, 335-345. -   Liu, Chun Yi & Aika, K.-i., 2004. Ammonia absorption on alkaline     earth halides as ammonia separation and storage procedure. Bull.     Chem. Soc. Jpn. 77 (1), 123-131. -   Lu, Hui-Bo; Mazet, N., Spinner, B., 1996. Modelling of gas-solid     reaction coupling of heat and mass transfer with chemical reaction.     Chem. Eng. Sci. 51 (15), 3829-3845. -   Matsumoto, S., 1997. Recent advances in automobile exhaust catalyst.     Catalysis Surveys from Japan 1, 111-117. -   Olovsson, I., 1965. Packing principles in the structures of metal     ammine salts. Acta Cryst. 18, 889-8.93. -   CRC Handbook, 2004. Handbook of chemistry and physics (web edition).     Gmelins Handbuch, 1939. Magnesium teil b: Die verbindungen des     magnesiums (27). -   The European Parliament, 1998. Directive 98/69/ec. -   The European Parliament, 1999. Directive 1999/96/ec. -   The European Parliament, 2003. Directive 2003/17/ec. -   Touzain, P., Moundamga-lniamy, 1994. Thermochemical     heattransformation: -   Study of the ammonia/magnesium chloride-GIC pair in a laboratory     pilot. Mol. Crys. Liq. Cryst. 245, 243-248. 

1. A solid ammonia storage and delivery material capable of absorption/desorption of ammonia and comprising: an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg, and wherein the ammonia storage and delivery material has been saturated with ammonia and compressed to a density of 0.9 to 1.3 g/cm³ and a bulk density above 70% of the skeleton density.
 2. A solid ammonia storage material as claimed in claim 1 wherein the anion is selected from fluoride, chloride, bromide, iodide, nitrate, thiocyanate, sulphate, molybdate, and phosphate ions.
 3. A solid ammonia storage material as claimed in claim 2 wherein the anion is the chloride.
 4. A solid ammonia storage material as claimed in claim 3 wherein the salt is Mg(NH₃)₆Cl₂.
 5. A solid ammonia storage material as claimed in claim 1, wherein the solid storage material has a density of 0.9 to 1.3 g/cm³.
 6. A solid ammonia storage material as claimed in claim 1, wherein the solid storage material has a density of 1.1 to 1.3 g/cm³.
 7. A solid ammonia storage material as claimed in claim 1, wherein the solid storage material has bulk density above 85% of the skeleton density.
 8. A method of producing a solid ammonia storage material capable of absorption/desorption of ammonia and comprising: an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said method comprising the steps of 1) providing the solid salt, 2) saturating the salt fully with ammonia, and 3) compressing the saturated ammonia salt complex to a bulk density above 70% of the skeleton density.
 9. A method as claimed in claim 8, wherein the ammonia salt complex is compressed to a bulk density above 80% of the skeleton density.
 10. A method as claimed in claim 9, wherein the ammonia salt complex is compressed to a bulk density above 85% of the skeleton density.
 11. A method for selective catalytic NO_(x) reduction in waste gases containing oxygen, using ammonia and a reduction catalyst wherein gaseous ammonia is provided by heating a solid storage medium capable of absorption/desorption of ammonia and comprising one or more ionic ammonia absorbing salts of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkaline earth metals, and transition metals such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions such as chloride or sulphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg, wherein the ammonia storage and delivery material has been saturated with ammonia and compressed to a bulk density above 70% of the skeleton density and wherein the release rate of ammonia is controlled in consideration of the content of NO_(x) in the waste gases.
 12. A method for selective catalatic reduction (SCR) of NO_(x) in exhaust gases from combustion processes comprising contacting an exhaust gase with a solid ammonia storage material capable of absorption/desorption of ammonia and comprising: an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkaline earth metals, and transition metals such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions such as chloride or sulphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg and wherein the ammonia storage and delivery material has been saturated with ammonia and compressed to a bulk density above 70% of the skeleton density as a source of ammonia as the reducing agent in selective catalytic reduction (SCR) of NO_(x) in exhaust gases from combustion processes.
 13. An ammonia delivery device comprising a container comprising an ammonia absorbing salt capable of absorption/desorption of ammonia, wherein the ammonia absorbing salt is an ionic salt of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg and wherein the ammonia storage and delivery material has been saturated with ammonia and compressed to a bulk density above 70% of the skeleton density, said container being provided with one or more closable outlet opening(s) connected to a pipe and further being provided with means for heating the container and the ammonia absorbing salt for release of gaseous ammonia.
 14. An ammonia delivery device as claimed in claim 13, wherein the closure of the closable outlet opening(s) is (are) in the form of one or more valve(s).
 15. An ammonia delivery device as claimed in claim 13, wherein the heating means is in the form of an electrical resistive heating device.
 16. An ammonia delivery device as claimed in claim 13, wherein said means for heating is provided by a heat produced by chemical reactions.
 17. An ammonia delivery device as claimed in claim 13, wherein the release rate of ammonia is controlled by accurate control of the heating of the container and the ammonia absorbing salt for release of gaseous ammonia.
 18. An ammonia delivery device as claimed in claim 13, where the release of ammonia is further controlled by reduction valves, flow controllers or similar.
 19. A method for selective catalytic reduction (SCR) of NO_(x) in exhaust gases from combustion processes comprising contacting an exhaust gase with an ammonia delivery device comprising a container comprising an ammonia absorbing salt capable of absorption/desorption of ammonia, wherein the ammonia absorbing salt is an ionic salt of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkaline earth metals, and/or one or more transition metals, such as Mn, Fe, Co, Ni, Cu, and/or Zn, X is one or more anions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, wherein M is Mg and wherein the ammonia storage and delivery material has been saturated with ammonia and compressed to a bulk density above 70% of the skeleton density, said container being provided with one or more closable outlet opening(s) connected to a pipe and further being provided with means for heating the container and the ammonia absorbing salt for release of gaseous ammonia as a source for ammonia in selective catalytic reduction of NO_(x) in exhaust gases from combustion processes.
 20. A solid ammonia storage and delivery material capable of absorption/desorption of ammonia and comprising: an ammonia absorbing salt, wherein the ammonia absorbing salt is an ionic salt of the general formula: M_(a)(NH₃)_(n)X_(z), wherein M is one or more cations selected from alkali metals, alkaline earth metals, and transition metals such as Li, Na, K, Cs, Mg, Ca, V, Cr, Mn, Fe, Co, Ni, Cu, or Zn or combinations thereof such as NaAl, KAl, K₂Zn, CsCu, or K₂Fe, X is one or more anions selected from fluoride, chloride, bromide, iodide, nitrate, thiocyanate, sulphate, molybdate, and phosphate ions, a is the number of cations per salt molecule, z is the number of anions per salt molecule, and n is the coordination number of 2 to 12, said storage and delivery material having been saturated with ammonia and compressed to a bulk density above 70% of the skeleton density and a density of 0.9 to 1.3 g/cm³.
 21. A solid ammonia storage material as claimed in claim 20, wherein the solid storage material has a density of 1.1 to 1.3 g/cm³. 